Ti-1300钛合金挤压管材组织性能研究

通过室温拉伸测试和显微组织观察，研究了挤压温度和热处理工艺对Ti-1300钛合金挤压管材显微组织和力学性能的影响，讨论了热加工工艺、显微组织和力学性能之间的关系。结果表明：Ti-1300钛合金在两相区挤压后的横向组织均匀细小，纵向组织沿挤压加工流线破碎均匀；其拉伸强度高达1 445 MPa。管材在相变点以上的高温固溶组织主要由等轴β相晶粒组成，具有较好的塑性。合金两相区挤压后具有较好的强度和塑性的匹配，两相区挤压的塑性明显优于β单相区挤压，尤其面缩。试样经过固溶时效处理后显微组织明显细化，强度大幅度提高，可达1 300 MPa以上。     

动车组车体底边梁用6005A铝型材检验分析

6005A铝合金大截面复杂制品作为轨道车体的边梁或枕梁，对轨道车体的整体起连接和承重作用，是动车组车体的关键部位。采用电子万能试验机、铝型材压力试验机、光学显微镜等研究了速度达400 km·h^-1动车组车体底边梁用6005A铝型材的强度、显微组织和断口形貌等，旨在为动车组用铝挤压型材产品检验和工艺制度制定提供技术支持与指导。     

6063铝合金表面点状物的分析研究

利用金相显微镜(OM)、扫描电子显微镜(SEM)和能谱分析仪(EDS)等分析研究了6063铝合金表面点状凸起物的表面形貌及成分.结果表明,这种点状凸起物主要是由大量聚集的碳化硅颗粒以及少量的游离硅组成,碳化硅颗粒硬度较大,不易加工,从而造成铝合金表面异常.     

Synthesis of aluminum nitride in a coke-calcium reduction bed using nitrogen in air

An experimental study on the heating of a mixture of aluminum and lithium hydroxide (LiOH) powders in a reductive bed under air atmosphere is reported. The formation of aluminum nitride (AlN) during this process was the focus of this study. The formation of AlN was achieved using LiOH as an additive and heating the sample in a resistance furnace in a specially designed double crucible within a bed of a mixture of coke and filamentous calcium. The temperature range of the reaction was between 700°C and 1100°C. The optimum tem-perature of 1100°C and the optimum LiOH amount (5wt%) required to achieve maximum yield were determined by powder X-ray diffrac-tion (XRD) analysis. Scanning electron microscopy (SEM) micrographs clearly indicated the transformation of grain structures from rods (700°C) to cauliflower shapes (1100°C).     

Microstructure,mechanical properties and wear resistance of an Al–Mg–Si alloy produced by equal channel angular pressing

Microstructure, mechanical properties and wear resistance in an ultrafine-grained Al–Mg–Si alloy fabricated utilizing a combination of equal channel angular pressing (ECAP) and dynamic aging were investigated in this paper. The results indicated that the grain size of the ECAP alloy was significantly refined, i.e., to ~239 nm after three ECAP passes. Meanwhile, the yield and tensile strength of the ECAPed material reached 340 MPa and 445 MPa, respectively, while maintaining a significant uniform elongation of 14%. Wear resistance results demonstrated that the wear rate, wear depth and width of the ECAPed material decreased in comparison with the solution-treated (SST) and peak-aged (T6) conditions under a load range of 5–25 N. The adhesive wear that occurs in the undeformed specimens at 10 N does not appear in the ECAPed specimen at the same load, indicating that the ECAPed specimen delay the appearance of more serious wear mechanisms under certain loads. The cooperative interaction of high density nano-scale β" precipitates and dislocations resulted in a combination of super-high strength and good work hardening ability which suppressed the extension of cracks between the friction layer and the plastic deformation zone. As a consequence, the combination of ECAP and dynamic aging brings a significant improvement for antifriction performance of the 6061 aluminum alloy.     

铝合金PLC效应与声发射特性的实验研究

考虑退火温度和应变率对6063铝合金力学性能的影响,采用材料试验机和声发射测试系统对铝合金PLC效应和声发射特性开展实验研究,获得了不同应变率下材料的应力-应变曲线和不同退火温度下声发射参数的变化规律.结果表明,2×10-3,2×10-4,2×10-5s-1应变率加载时,6063铝合金的应力应变曲线表现出明显的PLC现象,降低加载应变率,PLC现象增强,并出现了从A型到C型的转化;加载应变率为2×10-4s-1时,PLC效应的临界应变随退火温度的升高而降低;由于细观结构上可动位错密度的增加,屈服阶段试件中产生的声发射振铃计数急剧增加,达到峰值;进入到塑性强化阶段,声发射活动减弱;弹性变形阶段和塑性强化阶段产生突发型信号,而屈服阶段为连续型信号,与试件的均匀变形以及剪切变形带的形成与传播相关.      

铝、硅添加对方镁石-铝镁尖晶石质免烧耐火材料性能的影响

采用电熔镁砂和电熔尖晶石为主要原料,以葡萄糖和水合硫酸铝为复合结合剂,以金属铝粉和单质硅为添加剂,制备方镁石-铝镁尖晶石质免烧耐火材料,研究了不同热处理温度下铝加入量及硅铝复合添加对耐火材料显微结构、烧结性能及力学性能的影响。结果表明,随着铝粉加入量的增加,方镁石-铝镁尖晶石免烧耐火材料经不同温度处理后的线膨胀率、常温抗折强度和常温耐压强度增加,并且高温抗折强度也不断提高;另外,金属铝和单质硅的添加会引起耐火材料在升温过程中的增重并减少材料的体积膨胀,从而进一步提高材料的常温力学性能。     

花键冷挤压成形过程凹模入口半角优化数值模拟

以花键挤压成形过程为研究对象,利用DEFORM-3D软件对花键的冷挤压成形过程进行模拟;以金属流动、变形程度、成形载荷和模具磨损等作为花键成形过程中的衡量指标,分别设定15°、20°、22.5°、25°和30°的不同凹模入口半角,模拟分析对花键冷挤压成形过程的影响。模拟结果表明,凹模入口半角为20°时,花键的整体成形质量最好。     

泡沫铝合金孔隙率对泡沫铝合金/聚甲醛互穿复合材料的影响

使用硅烷偶联剂KH570对孔隙率不同的泡沫铝合金进行表面改性后,通过注塑成型法制备了聚甲醛/泡沫铝合金互穿复合材料。研究了改性后泡沫铝合金表面的红外结构、泡沫铝合金/聚甲醛互穿复合材料的力学性能和摩擦学性能以及泡沫铝合金/聚甲醛互穿复合材料的磨损表面。研究结果表明,硅烷偶联剂KH570成功接枝到了泡沫铝合金的表面;复合材料的弯曲强度和压缩强度随着泡沫铝合金孔隙率的降低而升高;而复合材料的摩擦学性能随着泡沫铝合金孔隙率的增加而降低。     

二乙基次膦酸铝的热分解动力学研究

以TG-DTG为手段,研究二乙基次膦酸铝阻燃剂在氮气气氛中的热分解动力学;利用Kissinger-Akahira-Sunose(KAS)法、Flynn-Wall-Ozawa(FWO)法对其进行热分解动力学研究,计算出该阻燃剂的平均热分解表观活化能分别为260.2和259.4 kJ/mol;利用atava-estk法研究该阻燃剂的热分解机理属于相边界反应,得到其热分解动力学方程为g(α)=1-(1-α)1/3。